SINTESIS DAN KARAKTERISASI TiO2-Fe DENGAN METODE HIDROTERMAL UNTUK FOTODEGRADASI PADA PENGOLAHAN LIMBAH LAUNDRY
Penulis :
NOVIALIS DAYUMITA
Abstrak :
ABSTRAK SINTESIS DAN KARAKTERISASI TiO2-Fe DENGAN METODE HIDROTERMAL UNTUK FOTODEGRADASI PADA PENGOLAHAN LIMBAH LAUNDRY Usaha jasa laundry merupakan salah satu solusi untuk mengatasi masalah perekonomian masyarakat. Seiring berjalannya waktu, usaha ini semakin banyak berkembang dan menimbulkan limbah cair yang mengandung bahan kimia seperti surfaktan, fosfat, ammonia, nitrogen, kadar padatan terlarut, kekeruhan, BOD dan COD yang tinggi. Metode pengolahan banyak dilakukan oleh peneliti lain, salah satunya fotokatalis. Penelitian ini bertujuan untuk mengolah limbah laundry melalui proses fotodegradasi dengan fotokatalis TiO2 yang didoping logam Fe dan disintesis menggunakan metode hidrotermal dengan tiga variasi Fe dari berat TiO2 10 gr yaitu 5%, 10% dan 15%. Fotokatalis dikarakterisasi dengan instrument XRD dan SEM-EDX. Berdasarkan hasil karakterisasi XRD, struktur kristal TiO2 adalah anatase, dibuktikan dengan adanya sudut difraksi 2? sesuai dengan JCPDS No 21-1272. Puncak difraksi dari Fe tidak terlalu signifikan, karena Fe telah tersubstitusi kedalam struktur kristal TiO2. Sedangkan pada hasil SEM, semakin tinggi konsentrasi Fe, maka morfologi sampel semakin tidak homogen, karena pengotor besi yang melebur saat proses pemanasan. Pengujian aktivitas fotokatalitik, dilakukan pada limbah Methylene Blue dan limbah cair laundry. Pada hasil pengujian Methylene Blue, fotokatalis N5 memiliki aktivitas fotodegradasi yang terbaik dan diaplikasikan pada limbah laundry dengan parameter COD, TSS dan pH. Didapatkan hasil pengujian pH adalah 7, nilai COD yaitu 654,53 mg/L dengan % fotodegradasi 27,7%, nilai TSS sebesar 196 mg/L dengan % fotodegradasi 20,96 %. Dari hasil penelitian tersebut, dapat disimpulkan bahwa fotokatalis TiO2-Fe N5 mampu menurunkan kadar COD dan TSS pada limbah laundry dengan proses fotokatalitik. Kata Kunci : Limbah Laundry, Fotodegradasi, Fotokatalis, TiO2-Fe
Abstrak Inggris :
ABSTRACT SYNTHESIS AND CHARACTERIZATION OF TiO2-Fe WITH HYDROTERMAL METHOD FOR PHOTODEGRADATION IN LAUNDRY WASTE TREATMENT Laundry service business is one solution to overcome communit economic problems. Over time, this business is growing and produced liquid waste containing chemicals such as surfactans, phosphates, ammonia, nitrogen, dissolved solid, turbidity, high BOD and COD. Many other researchers have used processing methods, one of which is as photocatalyst. This study aims to treat laundry waste through a photodegradation process with TiO2 photocatalyst doped with Fe and metal synthesized using the hydrothermal method with three variations of Fe from 10 gr TiO2 weight, namely 5%, 10% and 15%. Photocatalyst were characterized by XRD and SEM-EDX instruments. Based on the results of XRD characterization, the crystal structure of TiO2 is anatase, as evidenced by the presence of a diffraction angle of 2? according to JCPDS No. 21-1272. The diffraction peak of Fe is not very significant, because Fe has been substituted into the crystal structure of TiO2. Meanwhile, in SEM results the higher the Fe concentration, the more inhomogeneous of the sample, due to iron impurities that melt during the heating process. Photocatalyst activity testing was carried out on Methylene Blue waste and laundry liquid waste. In the Methylene Blue test result, N5 photocatalyst has the best photodegradation activity and is applied to laundry waste with COD, TSS and pH parameters. The results of the pH test were 7, the COD value was 654,53 mg/L with % photodegradation 27,7%, the TSS value was 196 mg/L with % photodegradation 21 %. From the results of this study, it can be concluded that the TiO2-Fe N5 photocatalyst is able to reduce the levels of COD and TSS in laundry waste with a photocatalytic process. Keyword : Laundry waste, Photodegradation, Photocatalyst, TiO2-Fe.
Tahun :
2022
Bab 1 :
Bab 5 :
Na :
A



UPT. Perpustakaan & UPT. TIPD UMRI

  • Kampus Utama : Jl. Tambusai / Jl. Nangka, Kecamatan Tampan
  • Kota Pekanbaru, Provinsi Riau

    E-Mail : pustaka@umri.ac.id - Website : http://lib.umri.ac.id - Smart Library : http://smartlib.umri.ac.id - Jurnal : http://jurnal.umri.ac.id

    Smartlib v1.3 © 2019 UPT TIPD UMRI. All Rights Reserved.