Karakteristik Sifat Fisis Dan Mekanis Genteng Polimer Dengan Penambahan Serat Sisal Sebagai Pengisi
Penulis :
SUCI RAMADHANI
Abstrak :
ABSTRAK KARAKTERISTIK SIFAT FISIS DAN MEKANIS GENTENG POLIMER DENGAN PENAMBAHAN SERAT SISAL SEBAGAI PENGISI Penelitian ini telah berhasil membuat genteng polimer menggunakan serat sisal, pasir, limbah botol plastik polyethylene terephtalate (PET) dengan campuran aspal dan pasir. Penelitian ini dilakukan untuk mengetahui karakteristik sifat fisis dan sifat mekanis genteng polimer. Perbandingan massa bahan yang digunakan adalah 10% aspal: 55% PET untuk variabel tetap, sedangkan variabel bebas untuk perbandingan pasir dan serat sisal yaitu 0% : 87,5%, 21,87% : 65,63%, 43,75% : 43,75%, 65,63% : 21,87%, 87,5% : 0%. Proses pembuatan dan pencetakan genteng menggunakan metode hotpress. Pengujian yang dilakukan meliputi sifat fisis yaitu kerapatan (density), porositas dan daya serap air (water absorption), sifat mekanis meliputi uji kuat lentur (bending test) dan uji kuat tarik (tensile test). Hasil penelitian menunjukkan bahwa genteng yang mempunyai hasil paling optimum adalah genteng dengan perbandingan 21,87% pasir : 65,63% serat sisal pada sampel 2 dengan nilai kerapatan 1,2543 gr/?cm?^3, porositas 0,065%, daya serap air 0,052%, uji lentur 2,77 Mpa, dan uji tarik 0,66 Mpa, hal ini dikarenakan sampel 2 menggunakan jumlah serat sisal sebanyak 65,63% optimum mengisi rongga pada pembentukan genteng polimer dikarenakan ukuran butir serat sisal 100 mesh lebih kecil dibandingkan ukuran butir pasir yaitu 50 mesh. Pengujian mekanis pada penelitian ini yang meliputi uji lentur telah memenuhi SNI 2095:1998 sedangkan pada uji tarik belum memenuhi ASTM D 638 03. Kata kunci : Genteng polimer, Serat Sisal, polyethylene terephtalate (PET)
Abstrak Inggris :
ABSTRACT CHARACTERISTICS OF THE PHYSICAL AND MECHANICAL PROPERTIES OF POLYMER TILES WITH THE ADDITION OF SISAL FIBERS AS FILLERS This research has succeeded in making polymer tiles using sisal fibers, sand, polyethylene terephtalate (PET) plastic bottle waste with a mixture of asphalt and sand. This research was conducted to find out the characteristics of physical properties and mechanical properties of polymer tiles. The ratio of the mass of the material used is 10% asphalt: 55% PET for fixed variables, while the free variable for sand and sisal fiber comparison is 0%: 87.5%, 21.87%: 65.63%, 43.75%: 43.75%, 65.63%: 21.87%, 87.5%: 0%. The process of making and printing tiles using the hotpress method. The tests carried out include physical properties,density, porosity and water absorption,mechanical properties including bending test) and tensile test. The results showed that the tile that had the most optimum result was a tile with a ratio of 21.87% sand: 65.63% sisal fiber in sample 2 with a density value of 1.2543 gr/?cm?^3 , porosity 0.065%, water absorption 0.052%, flexure test 2.77 Mpa, and tensile test 0.66 Mpa, this is because sample 2 uses the amount of sisal fiber as much as 65.63% optimum fill the cavity in the formation of polymer tile because the grain size of sisal fiber 100 mesh is smaller than the size of sand grains, which is 50 mesh. Mechanical testing in this study which includes flexure tests has met SNI 2095:1998 while the tensile test has not met ASTM D 638 03. Keywords: Polymer tile, Sisal Fiber, polyethylene terephtalate (PET)
Tahun :
2022
Cover :
Bab 1 :
Bab 5 :
Na :
A



UPT. Perpustakaan & UPT. TIPD UMRI

  • Kampus Utama : Jl. Tambusai / Jl. Nangka, Kecamatan Tampan
  • Kota Pekanbaru, Provinsi Riau

    E-Mail : pustaka@umri.ac.id - Website : http://lib.umri.ac.id - Smart Library : http://smartlib.umri.ac.id - Jurnal : http://jurnal.umri.ac.id

    Smartlib v1.3 © 2019 UPT TIPD UMRI. All Rights Reserved.