190204025
Judul :
SINTESIS DAN KARAKTERISASI MEMBRAN POLIMER ELEKTROLIT BERBASIS IOTA KARAGENAN DENGAN LITIUM HIDROKSIDA
Penulis :
KHAIRUNISA PUTRI
Abstrak :
SINTESIS DAN KARAKTERISASI MEMBRAN POLIMER ELEKTROLIT BERBASIS IOTA KARAGENAN DENGAN LITIUM HIDROKSIDA Penelitian ini bertujuan untuk mensintesis dan mengkarakterisasi membran polimer elektrolit berbasis iota karagenan dengan litium hidroksida sebagai bahan elektrolit untuk aplikasi baterai litium. Membran dibuat dengan metode solution casting menggunakan variasi komposisi iota karagenan dan litium hidroksida, serta ditambahkan glutaraldehide sebagai bahan taut silang. Karakterisasi yang dilakukan meliputi uji sifat mekanik yaitu kuat tarik, elongasi, dan ketebalan berdasarkan ASTM D-638, uji biodegradasi, dan karakterisasi konduktivitas menggunakan Electrochemical Impedance Spectroscopy (EIS). Hasil penelitian menunjukkan bahwa variasi terbaik pembuatan membran yaitu pada komposisi iota karagenan 100% yang menghasilkan lembaran tipis berwarna putih bening dengan permukaan halus. Nilai kuat tarik tertinggi diperoleh pada komposisi iota karagenan 60% dengan litium hidroksida 40% sebesar 53,5114 MPa, nilai elongasi tertinggi 23,11% pada komposisi yang sama, dan nilai ketebalan terbaik 0,163 mm pada komposisi iota karagenan 50% dengan litium hidroksida 50%. Uji biodegradasi menunjukkan bahwa semua variasi membran dapat terdegradasi dalam waktu 9 hari. Kata kunci: iota karagenan, litium hidroksida, membran polimer elektrolit, biodegradable, baterai litium
Abstrak Inggris :
SYNTHESIS AND CHARACTERIZATION OF IOTA-CARRAGEENAN-BASED POLYMER ELECTROLYTE MEMBRANES WITH LITHIUM HYDROXIDE This study aims to synthesize and characterize iota carrageenan-based polymer electrolyte membranes with lithium hydroxide as the electrolyte material for lithium battery applications. The membranes were prepared using the solution casting method with variations in the composition of iota carrageenan and lithium hydroxide, and glutaraldehyde was added as a cross-linking agent. The characterization included mechanical property tests such as tensile strength, elongation, and thickness based on ASTM D-638, a biodegradation test, and conductivity characterization using Electrochemical Impedance Spectroscopy (EIS). The results showed that the best membrane variation was obtained with 100% iota carrageenan composition, producing a thin, clear white sheet with a smooth surface. The highest tensile strength value was 53.5114 MPa and the highest elongation value was 23.11%, both obtained at a composition of 60% iota carrageenan with 40% lithium hydroxide. The best thickness value of 0.163 mm was obtained at a composition of 50% iota carrageenan with 50% lithium hydroxide. The biodegradation test showed that all membrane variations could degrade within 9 days. Keywords : Iota carrageenan, lithium hydroxide, polymer electrolyte membrane, biodegradable, lithium battery.
Tahun :
2023
Na :
A
Loading, updating changes...



UPT. Perpustakaan & UPT. TIPD UMRI

  • Kampus Utama : Jl. Tambusai / Jl. Nangka, Kecamatan Tampan
    • Kota Pekanbaru, Provinsi Riau

    E-Mail : pustaka@umri.ac.id - Website : http://lib.umri.ac.id - Smart Library : http://smartlib.umri.ac.id - Jurnal : http://jurnal.umri.ac.id

    Smartlib v1.3 © 2019 UPT TIPD UMRI. All Rights Reserved.